I am posting some answers to an email I received from someone interested in the boat. If anyone else has any questions, feel free to post!
Thanks! See below...
Looking over the pictures, I have some questions regarding the SeaCraft.
1. Have you separated the deck from the stringers?
Yes
2. What condition are the stringers in? Is the foam water logged?
The foam stringers are dry. I drilled a few pilot holes into the foam and all of the shavings were dry (I glassed back over the holes afterwards). The center stringer is made of wood; I'm not sure of the condition as I was planning to replace it. However, when I removed the old transom and removed a section of the stringer for access, the wood was solid.
3. What is the condition of the exterior hull? Are there any deep gouges in the gelcoat into the glass?
The exterior is fine.
4. Bottom condition? Are there any deep gouges or cracks? Or just the normal scratches from normal use?
There are some gouges in the bottom going into the fiberglass. I've used the boat for years like this, so I'm sure the repairs will be minor. No cracks.
5. On the board for the transom, what was the issue with the resin? What type of resin are you using, Epoxy or Polyester?
I'm using Boatyard Polyester Resin. I probably used too much hardener. This is hard to explain but I was sealing the edges of the board into the transom. I put a layer of chopped glass and resin into the transom and then put a layer of mat on the board. By the time I was ready to put the board into the transom, the chopped glass was already hard. So I just pulled the mat off of the board and called it a day. In short the board is fine but the transom will need some grinding to remove the chopped glass.
6. Is the transom board still usable?
Yes, there is a picture of it in my post in the CSC forum.
7. How road worthy is the trailer? Bearings, springs, hubs and tires? Bunks? Are both fenders missing?
The trailer is fine. The suspension, hubs, and wheels were replaced about a year ago. The fenders have been missing since I could remember.
|