Quote:
Originally Posted by Jared
Nice buy. I have been running a syncrowave 250 for a handful of years at work and added a dynasty 210 last year for something a little more portable. It’s a very nice machine, I would love to have a 280 like yours or 350 for the occasional heavy wall aluminum project I get.
I used 3/32 ER5356 filler, 3/32” 2% thoriated tungsten. Pulsed at 0.7 PPS, 190 amps peak, 30% background voltage, 30% peak time. Balance 65% freq 80H. These are settings I have landed on that make me 75% happy on the .125” 5052 I did the tank out of, but I always feel like something is off a tiny bit to get that last bit of quality I’m looking for.
|
I takes a good hand to keep up with the pulser. On mishap and your trying to catch back up. Looks really good judging by the one pic. I like to use pulse on some things and have used it at .7pps going down outside corners like that. Really makes a consistent looking weld. I have got used to having a momentary switch on my ck 20 water cooled rig now and can pulse manually as needed with the button. Doing stuff where it is hard to keep up with a foot petal the micro switch really shines. My father dose anodized T-tops and tuna towers and I learned from him so I guess that's where I picked up on that as most of them guys manually pulse.
I can say one thing I really like that has helped me is the amplitude settings. The dynasty 210/280 has them like the 350/400 if you pay the extra $500 for the SD card add on. I have been running higher EP around 180a and 150a EN on advanced square wave and was able to turn my balance up to 80-85% and still get a good cleaning action. The miller manual suggest running higher EN for more penetration but I have found if I do the opposite I can use less cleaning on the balance control and keep the heat out of my tungsten. I also run 120hz on the thinner materials (1/8") but stay at 80hz for just about everything else over that thickness. Now if I was doing a thick casting, then I may go lower turning it down to 50hz and use 25% helium 75% argon mix. The helium really helps and makes the 280 feel like a much bigger machine. It acts almost like a 350 on stright argon. Sometimes I even use the 25% helium mix on thinner stuff as well. I can cut the amps back by 30% and it still welds hot. Something about it really helps clean the puddle up and gives you a nice clean looking weld. I used to have a HTP 200 and you just about had to run mixed gas to do 1/4" material with it do to running out of amperage. It would do good with your 210 in the field if on a 120v extension cord and you could get a small 80cf bottle of 25%he to carry remotely.
The newer inverter machines have so many settings it is amazing what you can do with them. I also have a Lincoln tig 300/300 (375 amp) HF machine. There is no balance no frequency controls just basic 60 hz but you can really throw the heat on thicker materials. It dose a good job and is a tank at 800lbs. The more I play with the bells and whistles of the new dynasty's the more I like them though.